791539
Titania paste, reflector
Manufacturer: Sigma Aldrich
Synonym(S): Greatcell Solar® WER2-O, TiO2 paste
Select a Size
| Pack Size | SKU | Availability | Price |
|---|---|---|---|
| 5 G | 791539-5-G | In Stock | ₹ 13,693.63 |
| 20 G | 791539-20-G | In Stock | ₹ 35,516.83 |
791539 - 5 G
In Stock
Quantity
1
Base Price: ₹ 13,693.63
GST (18%): ₹ 2,464.853
Total Price: ₹ 16,158.483
description
Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level
100
form
paste (white)
concentration
20.0 wt. % (+/- 1.2 wt%)
avg. part. size
150-250 nm (scatter)
viscosity
15000-25000 mPa.s (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1)
InChI
1S/2O.Ti
InChI key
GWEVSGVZZGPLCZ-UHFFFAOYSA-N
Related Products
Description
- General description: Titania paste, the reflector is a precursor for titania, that forms a mesoporous light scattering layer on the fluorine doped tin oxide (FTO) substrates. It is used in a variety of electrochemical devices to improve electron mobility and power efficiency.[1][2]
- Application: Light scattering titania paste can be coated on the primary transparent layer of TiO2 to form a bilayered titanium film. It can be used as a negative electrode for dye sensitized solar cells (DSSCs).[3][4][5]
- Legal Information: Product of Greatcell Solar® exclusive supplier of Sun2 products under license from EPFL. Greatcell Solar® is a registered trademark of Greatcell Solar
SAFETY INFORMATION
Pictograms
Signal Word
Warning
Hazard Statements
Precautionary Statements
P264 - P280 - P302 + P352 - P305 + P351 + P338 - P332 + P313 - P337 + P313
Hazard Classifications
Eye Irrit. 2 - Skin Irrit. 2
WGK
WGK 1
Flash Point(F)
195.8 °F
Flash Point(C)
91 °C
Compare Similar Items
Show Difference
description: Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level: 100
form: paste (white)
concentration: 20.0 wt. % (+/- 1.2 wt%)
avg. part. size: 150-250 nm (scatter)
viscosity: 15000-25000 mPa.s (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1)
InChI: 1S/2O.Ti
InChI key: GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description:
Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level:
100
form:
paste (white)
concentration:
20.0 wt. % (+/- 1.2 wt%)
avg. part. size:
150-250 nm (scatter)
viscosity:
15000-25000 mPa.s (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1)
InChI:
1S/2O.Ti
InChI key:
GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description: Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level: 100
form: paste (yellow)
concentration: 19.0 wt. %
avg. part. size: 20 nm (active)
viscosity: 40000-55000 mPa.s(20 °C) (Analysis carried out at 20°C with 20mm 4 degree cone/plate; 40 s-1))
InChI: 1S/2O.Ti
InChI key: GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description:
Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level:
100
form:
paste (yellow)
concentration:
19.0 wt. %
avg. part. size:
20 nm (active)
viscosity:
40000-55000 mPa.s(20 °C) (Analysis carried out at 20°C with 20mm 4 degree cone/plate; 40 s-1))
InChI:
1S/2O.Ti
InChI key:
GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description: Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level: 100
form: paste (cream)
concentration: 27.0 wt. %
avg. part. size: 20 nm (active)≤450 nm (scatter)
viscosity: 40000-55000 mPa.s(20 °C) (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1))
InChI: 1S/2O.Ti
InChI key: GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description:
Crystal Structure: > 99% anatase (analysis carried out on starting material, prior to paste manufacture)
Quality Level:
100
form:
paste (cream)
concentration:
27.0 wt. %
avg. part. size:
20 nm (active)≤450 nm (scatter)
viscosity:
40000-55000 mPa.s(20 °C) (Analysis carried out with 20mm 4 degree cone/plate; 40 s-1))
InChI:
1S/2O.Ti
InChI key:
GWEVSGVZZGPLCZ-UHFFFAOYSA-N
description: __
Quality Level: 100
form: powder
concentration: __
avg. part. size: __
viscosity: __
InChI: 1S/C6H11O9P/c7-3(1-4(8)6(10)11)5(9)2-15-16(12,13)14/h3,5,7,9H,1-2H2,(H,10,11)(H2,12,13,14)/t3-,5+/m0/s1
InChI key: OVPRPPOVAXRCED-WVZVXSGGSA-N
description:
__
Quality Level:
100
form:
powder
concentration:
__
avg. part. size:
__
viscosity:
__
InChI:
1S/C6H11O9P/c7-3(1-4(8)6(10)11)5(9)2-15-16(12,13)14/h3,5,7,9H,1-2H2,(H,10,11)(H2,12,13,14)/t3-,5+/m0/s1
InChI key:
OVPRPPOVAXRCED-WVZVXSGGSA-N